作者范勇,郭佳,陈昊,杨瑞宵,杨书宇（2019）在《纳米Al2O3改性聚酯亚胺介电性能》一文中研究指出：为了提高聚酯亚胺树脂耐电晕性能,采用微乳化-相转变法制备纳米Al2O3溶胶,并通过机械共混,使其分散到聚酯亚胺树脂溶液中,制备了纳米Al2O3杂化聚酯亚胺复合材料。实验结果表明:纳米粒子在聚酯亚胺基体中分散均匀;随掺杂量的提高,复合材料的耐电晕性呈上升趋势,但介电强度呈下降趋势,当纳米掺杂质量分数为12%时,耐电晕寿命达到纯聚酯亚胺树脂的5倍,介电强度达到175.2 kV/mm;纳米Al2O3对复合材料的介电损耗影响很小,但介电系数随掺杂量增加而略有升高;引入纳米Al2O3对材料耐热性影响不大。
Abstract
wei le di gao ju zhi ya an shu zhi nai dian yun xing neng ,cai yong wei ru hua -xiang zhuai bian fa zhi bei na mi Al2O3rong jiao ,bing tong guo ji xie gong hun ,shi ji fen san dao ju zhi ya an shu zhi rong ye zhong ,zhi bei le na mi Al2O3za hua ju zhi ya an fu ge cai liao 。shi yan jie guo biao ming :na mi li zi zai ju zhi ya an ji ti zhong fen san jun yun ;sui can za liang de di gao ,fu ge cai liao de nai dian yun xing cheng shang sheng qu shi ,dan jie dian jiang du cheng xia jiang qu shi ,dang na mi can za zhi liang fen shu wei 12%shi ,nai dian yun shou ming da dao chun ju zhi ya an shu zhi de 5bei ,jie dian jiang du da dao 175.2 kV/mm;na mi Al2O3dui fu ge cai liao de jie dian sun hao ying xiang hen xiao ,dan jie dian ji shu sui can za liang zeng jia er lve you sheng gao ;yin ru na mi Al2O3dui cai liao nai re xing ying xiang bu da 。
论文参考文献
论文详细介绍
论文作者分别是来自哈尔滨理工大学学报的范勇,郭佳,陈昊,杨瑞宵,杨书宇，发表于刊物哈尔滨理工大学学报2019年01期论文，是一篇关于聚酯亚胺论文,耐电晕论文,介电性能论文,哈尔滨理工大学学报2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自哈尔滨理工大学学报2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：聚酯亚胺论文; 耐电晕论文; 介电性能论文; 哈尔滨理工大学学报2019年01期论文;