本文主要研究内容
作者（2019）在《Microstructure and finite element analysis of hot continuous rolling of doped tungsten rod》一文中研究指出：The microstructures of doped tungsten deformed by multi-pass hot continuous rolling were investigated, and the stress and strain fields were simulated by finite element(FE) method. After the continuous rolling, the grains of the tungsten rod were refined, and the microhardness was improved; however, a ring region of abnormal grain growth was present at a distance of about 3/5 R(R is the radius of the rod) from the center of the cross section. FE modeling results showed that the equivalent residual strains were minimum around the region of abnormal grain growth; this was due to the release of strain energy by severe plastic deformation, leading a situation where the migration force of grain boundaries was higher than the pinning force of potassium bubbles. By decreasing the initial rolling temperature and rolling speeds, the inhomogeneity of the equivalent residual stain decreased, improving the microstructure uniformity of the doped tungsten.
Abstract
The microstructures of doped tungsten deformed by multi-pass hot continuous rolling were investigated, and the stress and strain fields were simulated by finite element(FE) method. After the continuous rolling, the grains of the tungsten rod were refined, and the microhardness was improved; however, a ring region of abnormal grain growth was present at a distance of about 3/5 R(R is the radius of the rod) from the center of the cross section. FE modeling results showed that the equivalent residual strains were minimum around the region of abnormal grain growth; this was due to the release of strain energy by severe plastic deformation, leading a situation where the migration force of grain boundaries was higher than the pinning force of potassium bubbles. By decreasing the initial rolling temperature and rolling speeds, the inhomogeneity of the equivalent residual stain decreased, improving the microstructure uniformity of the doped tungsten.
论文参考文献
论文详细介绍
论文作者分别是来自International Journal of Minerals Metallurgy and Materials的，发表于刊物International Journal of Minerals Metallurgy and Materials2019年03期论文，是一篇关于,International Journal of Minerals Metallurgy and Materials2019年03期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自International Journal of Minerals Metallurgy and Materials2019年03期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：International Journal of Minerals Metallurgy and Materials2019年03期论文;