作者赵燕青,孙力,梁爱国,田志强,陈振业,罗应明,杨浩（2019）在《淬火温度对780 MPa级Ti-Nb-B微合金化水电用钢组织和力学性能的影响》一文中研究指出：研究了淬火温度对780 MPa级水电用钢(/%:0.09C,0.10Si,1.50Mn,0.009P,0.002S,0.90Cr,0.20Ni,0.023Ti,0.004Nb,0.001 0B)组织和力学性能的影响。结果表明,试验钢不同温度淬火后均得到了板条贝氏体组织,随着淬火温度910℃升高至950℃,奥氏体平均晶粒从9.1μm长大到16.6μm,试验钢回火后基本保持了淬火态的板条结构。淬火温度在910～950℃试验钢的强度随着淬火温度的升高先增大后减小,并在930℃时达到最大,试验钢冲击韧性和断后延伸率与强度有着相同的变化规律。在930℃淬火,610℃回火的工艺参数条件下,获得最佳的力学性能:屈服强度为802 MPa,抗拉强度为858 MPa,伸长率为19%,-40℃冲击功为238 J。
Abstract
yan jiu le cui huo wen du dui 780 MPaji shui dian yong gang (/%:0.09C,0.10Si,1.50Mn,0.009P,0.002S,0.90Cr,0.20Ni,0.023Ti,0.004Nb,0.001 0B)zu zhi he li xue xing neng de ying xiang 。jie guo biao ming ,shi yan gang bu tong wen du cui huo hou jun de dao le ban tiao bei shi ti zu zhi ,sui zhao cui huo wen du 910℃sheng gao zhi 950℃,ao shi ti ping jun jing li cong 9.1μmchang da dao 16.6μm,shi yan gang hui huo hou ji ben bao chi le cui huo tai de ban tiao jie gou 。cui huo wen du zai 910～950℃shi yan gang de jiang du sui zhao cui huo wen du de sheng gao xian zeng da hou jian xiao ,bing zai 930℃shi da dao zui da ,shi yan gang chong ji ren xing he duan hou yan shen lv yu jiang du you zhao xiang tong de bian hua gui lv 。zai 930℃cui huo ,610℃hui huo de gong yi can shu tiao jian xia ,huo de zui jia de li xue xing neng :qu fu jiang du wei 802 MPa,kang la jiang du wei 858 MPa,shen chang lv wei 19%,-40℃chong ji gong wei 238 J。
论文参考文献
论文详细介绍
论文作者分别是来自特殊钢的赵燕青,孙力,梁爱国,田志强,陈振业,罗应明,杨浩，发表于刊物特殊钢2019年03期论文，是一篇关于微合金化论文,淬火温度论文,水电用钢论文,组织论文,力学性能论文,特殊钢2019年03期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自特殊钢2019年03期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。