作者高福洋,张毅,孙建刚,李要宗,袁博（2019）在《钛合金多层多道电弧增材制造成形特性研究》一文中研究指出：采用Ti6321A焊丝进行电弧增材制造,研究层与层、道与道之间的金相关系,表征多层多道增材组织特征,分析其对性能的影响规律。结果发现,交错式堆积方式获得的增材制造部件,成形良好,内部无缺陷。终道熔敷层,晶粒较为粗大,最后形成贯穿上下2层焊缝的柱状晶,内部主要为针状马氏体和残余β相;中部存在层间和道间2种位置结构,其中层间交界组织受到3次热循环,柱状晶被破碎,晶粒趋向于等轴晶,而且α相含量增多;而层间填充部分,由于冷却速度较快,高温停留时间较短,形成细小密集的魏氏组织;道间出现了较为明显的晶粒尺寸差异,这与道间温度过高、熔敷层表面出现凹坑、在2次填充时出现不同熔敷层"混层"现象有关。基板与增材界面热输入小,晶粒较为细小,同时由于后热作用晶粒得到一定程度的破碎,趋向于等轴化,而且进一步降低了界面处的应力水平。拉伸试验结果显示,增材制造材料的平均抗拉强度为870 MPa,断后伸长率为13.3%,上下2层增材制造的材料均匀性较好,没有上下层的明显差异,表现出稳定的力学性能。
Abstract
cai yong Ti6321Ahan si jin hang dian hu zeng cai zhi zao ,yan jiu ceng yu ceng 、dao yu dao zhi jian de jin xiang guan ji ,biao zheng duo ceng duo dao zeng cai zu zhi te zheng ,fen xi ji dui xing neng de ying xiang gui lv 。jie guo fa xian ,jiao cuo shi dui ji fang shi huo de de zeng cai zhi zao bu jian ,cheng xing liang hao ,nei bu mo que xian 。zhong dao rong fu ceng ,jing li jiao wei cu da ,zui hou xing cheng guan chuan shang xia 2ceng han feng de zhu zhuang jing ,nei bu zhu yao wei zhen zhuang ma shi ti he can yu βxiang ;zhong bu cun zai ceng jian he dao jian 2chong wei zhi jie gou ,ji zhong ceng jian jiao jie zu zhi shou dao 3ci re xun huan ,zhu zhuang jing bei po sui ,jing li qu xiang yu deng zhou jing ,er ju αxiang han liang zeng duo ;er ceng jian tian chong bu fen ,you yu leng que su du jiao kuai ,gao wen ting liu shi jian jiao duan ,xing cheng xi xiao mi ji de wei shi zu zhi ;dao jian chu xian le jiao wei ming xian de jing li che cun cha yi ,zhe yu dao jian wen du guo gao 、rong fu ceng biao mian chu xian ao keng 、zai 2ci tian chong shi chu xian bu tong rong fu ceng "hun ceng "xian xiang you guan 。ji ban yu zeng cai jie mian re shu ru xiao ,jing li jiao wei xi xiao ,tong shi you yu hou re zuo yong jing li de dao yi ding cheng du de po sui ,qu xiang yu deng zhou hua ,er ju jin yi bu jiang di le jie mian chu de ying li shui ping 。la shen shi yan jie guo xian shi ,zeng cai zhi zao cai liao de ping jun kang la jiang du wei 870 MPa,duan hou shen chang lv wei 13.3%,shang xia 2ceng zeng cai zhi zao de cai liao jun yun xing jiao hao ,mei you shang xia ceng de ming xian cha yi ,biao xian chu wen ding de li xue xing neng 。
论文参考文献
论文详细介绍
论文作者分别是来自焊接技术的高福洋,张毅,孙建刚,李要宗,袁博，发表于刊物焊接技术2019年05期论文，是一篇关于钛合金论文,增材制造论文,多层多道论文,成形特性论文,焊接技术2019年05期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自焊接技术2019年05期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：钛合金论文; 增材制造论文; 多层多道论文; 成形特性论文; 焊接技术2019年05期论文;