本文主要研究内容
作者吴玉厚,王浩,李颂华,王贺,孙健,王定文（2019）在《HIPSN陶瓷磨削力与温度的实验研究》一文中研究指出：为了研究磨削参数对热等静压氮化硅陶瓷磨削温度与磨削力的影响以及磨削温度和磨削力与表面形成之间的关系。通过正交实验得出磨削参数与磨削温度、磨削力以及比磨削能的关系,而后得出比磨削能与表面成形的关系。当砂轮速度由30 m/s增大到45 m/s,法向磨削力由241. 4 N减小到185. 3 N,切向磨削力由83. 5 N减小到58 N,磨削温度由268℃增加到370. 5℃,比磨削能由179. 14 J/mm-3增加到238. 88 J/mm-3,表面质量变好。磨削深度由5μm增加到35μm,法向磨削力由178. 15 N增加到274. 6 N,切向磨削力由40. 88 N增加到115 N,磨削温度由77. 75℃增加到593℃;比磨削能由335. 74 J/mm-3减小到100. 72 J/mm-3,表面质量变差。工件进给速度由1000 mm/min增大到7000 mm/min,法向磨削力由185. 13 N增加到256. 05 N,切向磨削力由47. 48 N增加到91. 08 N,磨削温度先由352. 25℃减小到308℃,后增加到325. 75℃,比磨削能由376. 2 J/mm-3减小到94. 98 J/mm-3,表面质量变差。当比磨削能较大时,表面以塑性变形的方式去除,比磨削能较小时,表面以脆性断裂的方式去除。在陶瓷磨削加工中尽可能选择小切深和较缓的工件进给速度,并适当提高砂轮线速度。
Abstract
wei le yan jiu mo xiao can shu dui re deng jing ya dan hua gui tao ci mo xiao wen du yu mo xiao li de ying xiang yi ji mo xiao wen du he mo xiao li yu biao mian xing cheng zhi jian de guan ji 。tong guo zheng jiao shi yan de chu mo xiao can shu yu mo xiao wen du 、mo xiao li yi ji bi mo xiao neng de guan ji ,er hou de chu bi mo xiao neng yu biao mian cheng xing de guan ji 。dang sha lun su du you 30 m/szeng da dao 45 m/s,fa xiang mo xiao li you 241. 4 Njian xiao dao 185. 3 N,qie xiang mo xiao li you 83. 5 Njian xiao dao 58 N,mo xiao wen du you 268℃zeng jia dao 370. 5℃,bi mo xiao neng you 179. 14 J/mm-3zeng jia dao 238. 88 J/mm-3,biao mian zhi liang bian hao 。mo xiao shen du you 5μmzeng jia dao 35μm,fa xiang mo xiao li you 178. 15 Nzeng jia dao 274. 6 N,qie xiang mo xiao li you 40. 88 Nzeng jia dao 115 N,mo xiao wen du you 77. 75℃zeng jia dao 593℃;bi mo xiao neng you 335. 74 J/mm-3jian xiao dao 100. 72 J/mm-3,biao mian zhi liang bian cha 。gong jian jin gei su du you 1000 mm/minzeng da dao 7000 mm/min,fa xiang mo xiao li you 185. 13 Nzeng jia dao 256. 05 N,qie xiang mo xiao li you 47. 48 Nzeng jia dao 91. 08 N,mo xiao wen du xian you 352. 25℃jian xiao dao 308℃,hou zeng jia dao 325. 75℃,bi mo xiao neng you 376. 2 J/mm-3jian xiao dao 94. 98 J/mm-3,biao mian zhi liang bian cha 。dang bi mo xiao neng jiao da shi ,biao mian yi su xing bian xing de fang shi qu chu ,bi mo xiao neng jiao xiao shi ,biao mian yi cui xing duan lie de fang shi qu chu 。zai tao ci mo xiao jia gong zhong jin ke neng shua ze xiao qie shen he jiao huan de gong jian jin gei su du ,bing kuo dang di gao sha lun xian su du 。
论文参考文献
论文详细介绍
论文作者分别是来自人工晶体学报的吴玉厚,王浩,李颂华,王贺,孙健,王定文，发表于刊物人工晶体学报2019年08期论文，是一篇关于磨削参数论文,磨削力论文,磨削温度论文,比磨削能论文,去除方式论文,人工晶体学报2019年08期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自人工晶体学报2019年08期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。