作者（2019）在《Grain boundary segregation and its influences on ionic conduction properties of scandia doped zirconia electrolytes》一文中研究指出：Solid oxide fuel cell is a promising energy conversion system which converts chemical energy into electrical energy directly. Electrolyte is the key component and determines the working temperature. In this paper,ceria and scandia co-doped zirconia electrolytes sintered from 1300 to 1550 ℃ were chosen as research objects. Scanning electron microscopy, X-ray diffraction and transmission electron microscopy were performed to characterize the ceramic samples. The effects of grain size and grain boundary element segregation on the electrical conductivity were focused. Electrochemical impedance spectroscopy was used to calculate the bulk, grain boundary and specific grain boundary conductivity. Results show that the bulk and grain boundary ionic conductivity increases with the increasing grain size.However, the specific grain boundary conductivity decreases with the increasing grain size. This is explained by the fact that Sc3+ is segregated at the grain boundary, which leads to higher oxygen vacancy concentration when sintered at lower temperature.
Abstract
Solid oxide fuel cell is a promising energy conversion system which converts chemical energy into electrical energy directly. Electrolyte is the key component and determines the working temperature. In this paper,ceria and scandia co-doped zirconia electrolytes sintered from 1300 to 1550 ℃ were chosen as research objects. Scanning electron microscopy, X-ray diffraction and transmission electron microscopy were performed to characterize the ceramic samples. The effects of grain size and grain boundary element segregation on the electrical conductivity were focused. Electrochemical impedance spectroscopy was used to calculate the bulk, grain boundary and specific grain boundary conductivity. Results show that the bulk and grain boundary ionic conductivity increases with the increasing grain size.However, the specific grain boundary conductivity decreases with the increasing grain size. This is explained by the fact that Sc3+ is segregated at the grain boundary, which leads to higher oxygen vacancy concentration when sintered at lower temperature.
论文参考文献
论文详细介绍
论文作者分别是来自Journal of Rare Earths的，发表于刊物Journal of Rare Earths2019年06期论文，是一篇关于,Journal of Rare Earths2019年06期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Journal of Rare Earths2019年06期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。