作者（2019）在《Preparation and Characteristics of Poly(butylene adipate-coterephthalate)/Polylactide Blend Films via Synergistic Efficiency of Plasticization and Compatibilization》一文中研究指出：Polylactide(PLA)films blended with poly(butylene adipate-co-terephthalate)(PBAT)were hot melted using a twin screw extruder with the addition of triethyl citrate(TEC)as a plasticizer and toluene diisocyanate(TDI)as a compatibilizer.The synergistic effects of the two additives on the mechanical,thermal,and morphological properties of the PLA/PBAT blend films were investigated.The influence of TEC content on the plasticized PLA films and the effect of TDI’s presence on the PLA/PBAT blend films were also studied by comparing them with neat PLA.The results showed a pronounced increase in elongation at break of the plasticized PLA films with increasing TEC levels,but a slight reduction in thermal stability.Also,the addition of TEC and TDI to the blend system not only synergistically enhanced the tensile properties and tensile-impact strength of the PLA/PBAT blends,but also affected their crystallinity and cold crystallization rate,a result of the improvement of interfacial interaction between PLA and PBAT,including the enhancement of their chain mobility.The synergy of the plasticization and compatibilization processes led to the improvement of tensile properties,tensile-impact strength,and compatibility of the blends,accelerating cold crystallization without affecting crystallization.
Abstract
Polylactide(PLA)films blended with poly(butylene adipate-co-terephthalate)(PBAT)were hot melted using a twin screw extruder with the addition of triethyl citrate(TEC)as a plasticizer and toluene diisocyanate(TDI)as a compatibilizer.The synergistic effects of the two additives on the mechanical,thermal,and morphological properties of the PLA/PBAT blend films were investigated.The influence of TEC content on the plasticized PLA films and the effect of TDI’s presence on the PLA/PBAT blend films were also studied by comparing them with neat PLA.The results showed a pronounced increase in elongation at break of the plasticized PLA films with increasing TEC levels,but a slight reduction in thermal stability.Also,the addition of TEC and TDI to the blend system not only synergistically enhanced the tensile properties and tensile-impact strength of the PLA/PBAT blends,but also affected their crystallinity and cold crystallization rate,a result of the improvement of interfacial interaction between PLA and PBAT,including the enhancement of their chain mobility.The synergy of the plasticization and compatibilization processes led to the improvement of tensile properties,tensile-impact strength,and compatibility of the blends,accelerating cold crystallization without affecting crystallization.
论文参考文献
论文详细介绍
论文作者分别是来自Chinese Journal of Polymer Science的，发表于刊物Chinese Journal of Polymer Science2019年01期论文，是一篇关于,Chinese Journal of Polymer Science2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Chinese Journal of Polymer Science2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。