本文主要研究内容
作者（2019）在《Modeling the Dynamic Recrystallization of Mg–11Gd–4Y–2Zn–0.4Zr Alloy Considering Non-uniform Deformation and LPSO Kinking During Hot Compression》一文中研究指出：Hot compression tests of Mg–11 Gd–4 Y–2 Zn–0.4 Zr alloy（GWZK114） were conducted at a deformation temperature range of 300–500 °C and a strain rate range of 0.01–10.0 s-1. Based on systematic microstructure observation, it is confirmed that long period stacking ordered（LPSO） phase displays essential and evolving roles on the dynamic recrystallization（DRX）behavior. The results indicate that the plastic deformation is mainly coordinated by simultaneous exist of LPSO kinking of lamella 14 H-LPSO phase and DRX at 350–450 °C, and DRX at 500 °C. Further, it is found that the LPSO kinking induced during 350–450 °C can delay the DRX. A phenomenological DRX model of GWZK114 alloy is established to be XDRX = 1. exp[-0.5（（ε-εc）/ε*）0.91]. Non-uniform distribution of plastic strain during compression was considered via finite element method and it ensures a good prediction of DRX fraction under a large plastic strain. Meanwhile, an enhanced DRX model, taking its formulation as XDRX = {1. exp[-0.5（（ε-εc）/ε*）0.91]}（ T/（226.8）-1）n, n = 3.82ε0.083, is proposed for the first time to capture the hindering effect of 14 H-LPSO kinking on DRX behavior. The predicted results of this enhanced DRX model agree well with the experimental cases, where 14 H-LPSO kinking is dominated or partially involved（300–450 °C）. Besides,a size model of DRX grains is also established and can depict the evolution of DRX grain size for all the investigated compression conditions with accounting for temperature rising at high strain rates（5 s-1 and 10 s-1）.
Abstract
Hot compression tests of Mg–11 Gd–4 Y–2 Zn–0.4 Zr alloy（GWZK114） were conducted at a deformation temperature range of 300–500 °C and a strain rate range of 0.01–10.0 s-1. Based on systematic microstructure observation, it is confirmed that long period stacking ordered（LPSO） phase displays essential and evolving roles on the dynamic recrystallization（DRX）behavior. The results indicate that the plastic deformation is mainly coordinated by simultaneous exist of LPSO kinking of lamella 14 H-LPSO phase and DRX at 350–450 °C, and DRX at 500 °C. Further, it is found that the LPSO kinking induced during 350–450 °C can delay the DRX. A phenomenological DRX model of GWZK114 alloy is established to be XDRX = 1. exp[-0.5（（ε-εc）/ε*）0.91]. Non-uniform distribution of plastic strain during compression was considered via finite element method and it ensures a good prediction of DRX fraction under a large plastic strain. Meanwhile, an enhanced DRX model, taking its formulation as XDRX = {1. exp[-0.5（（ε-εc）/ε*）0.91]}（ T/（226.8）-1）n, n = 3.82ε0.083, is proposed for the first time to capture the hindering effect of 14 H-LPSO kinking on DRX behavior. The predicted results of this enhanced DRX model agree well with the experimental cases, where 14 H-LPSO kinking is dominated or partially involved（300–450 °C）. Besides,a size model of DRX grains is also established and can depict the evolution of DRX grain size for all the investigated compression conditions with accounting for temperature rising at high strain rates（5 s-1 and 10 s-1）.
论文参考文献
论文详细介绍
论文作者分别是来自Acta Metallurgica Sinica(English Letters)的，发表于刊物Acta Metallurgica Sinica(English Letters)2019年09期论文，是一篇关于,Acta Metallurgica Sinica(English Letters)2019年09期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Acta Metallurgica Sinica(English Letters)2019年09期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。