作者（2019）在《Effects of Ce-rich RE on microstructure and mechanical properties of as-cast Mg-8Li-3Al-2Zn-0.5Nd alloy with duplex structure》一文中研究指出：The effects of Ce-rich RE on the microstructure and mechanical properties of as-cast Mg-8Li-3Al-2Zn-0.5Nd-x RE(x = 0, 1, 2, 3 wt%) alloys were investigated. The results indicated that the as-cast Mg-8Li-3Al-2Zn-0.5Nd alloy mainly consisted of α-Mg, β-Li, AlLi, MgLi2 Al and Al2 Nd phases. With the addition of Ce-rich RE in the alloy,Al3 RE and Al2 RE phases generated and gradually grew into net-like or block-like structure. With the addition of RE, Al-RE phases generated by consuming Al element and, thus, less Al element was dissolved in the matrix and less AlLi phase formed. Furthermore, less AlLi phase means that more Li element released to cause the increase ofβ-Li phase and refine the α-Mg phase. Under the influence of these factors, adding more RE led to higher elongation and lower tensile strength and hardness. With the addition of Ce-rich RE, the yield strength and ultimate tensile strength of the as-cast Mg-8Li-3Al-2Zn-0.5Nd alloy gradually decreased from 180 to 152 MPa and from 215 to 193 MPa, respectively, while the elongation was remarkably improved from 21.1% to 40.2%.
Abstract
The effects of Ce-rich RE on the microstructure and mechanical properties of as-cast Mg-8Li-3Al-2Zn-0.5Nd-x RE(x = 0, 1, 2, 3 wt%) alloys were investigated. The results indicated that the as-cast Mg-8Li-3Al-2Zn-0.5Nd alloy mainly consisted of α-Mg, β-Li, AlLi, MgLi2 Al and Al2 Nd phases. With the addition of Ce-rich RE in the alloy,Al3 RE and Al2 RE phases generated and gradually grew into net-like or block-like structure. With the addition of RE, Al-RE phases generated by consuming Al element and, thus, less Al element was dissolved in the matrix and less AlLi phase formed. Furthermore, less AlLi phase means that more Li element released to cause the increase ofβ-Li phase and refine the α-Mg phase. Under the influence of these factors, adding more RE led to higher elongation and lower tensile strength and hardness. With the addition of Ce-rich RE, the yield strength and ultimate tensile strength of the as-cast Mg-8Li-3Al-2Zn-0.5Nd alloy gradually decreased from 180 to 152 MPa and from 215 to 193 MPa, respectively, while the elongation was remarkably improved from 21.1% to 40.2%.
论文参考文献
论文详细介绍
论文作者分别是来自Progress in Natural Science:Materials International的，发表于刊物Progress in Natural Science:Materials International2019年01期论文，是一篇关于,Progress in Natural Science:Materials International2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Progress in Natural Science:Materials International2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：Progress in Natural Science:Materials International2019年01期论文;