本文主要研究内容
作者程春龙,乐启炽(2019)在《Al含量对AZ系镁合金燃点的影响》一文中研究指出:为了考察AZ系镁合金中不同Al含量对其初始熔化温度、燃点以及热解起燃时所处状态的影响,对镁合金初始熔化温度及燃点进行测试,采用FESEM扫描电镜对实验镁合金组织及燃烧前合金表面形貌进行观察,采用XRD对合金进行物相分析.结果表明,AZ系镁合金中Al含量较低时对燃点的影响表现为,随Al含量的增加低温熔点相β-Mg17Al12生成并逐渐增多,引起合金初始熔化温度的下降,降低了合金的燃点.同时,纯Mg及AZ31镁合金是在固态下起燃的; AZ61和AZ80镁合金是在半固态下起燃的,但AZ80的固相率更低.此外,Al含量的增加有利于合金起燃前表面膜的连续性与完整性,减缓合金燃点降低.
Abstract
wei le kao cha AZji mei ge jin zhong bu tong Alhan liang dui ji chu shi rong hua wen du 、ran dian yi ji re jie qi ran shi suo chu zhuang tai de ying xiang ,dui mei ge jin chu shi rong hua wen du ji ran dian jin hang ce shi ,cai yong FESEMsao miao dian jing dui shi yan mei ge jin zu zhi ji ran shao qian ge jin biao mian xing mao jin hang guan cha ,cai yong XRDdui ge jin jin hang wu xiang fen xi .jie guo biao ming ,AZji mei ge jin zhong Alhan liang jiao di shi dui ran dian de ying xiang biao xian wei ,sui Alhan liang de zeng jia di wen rong dian xiang β-Mg17Al12sheng cheng bing zhu jian zeng duo ,yin qi ge jin chu shi rong hua wen du de xia jiang ,jiang di le ge jin de ran dian .tong shi ,chun Mgji AZ31mei ge jin shi zai gu tai xia qi ran de ; AZ61he AZ80mei ge jin shi zai ban gu tai xia qi ran de ,dan AZ80de gu xiang lv geng di .ci wai ,Alhan liang de zeng jia you li yu ge jin qi ran qian biao mian mo de lian xu xing yu wan zheng xing ,jian huan ge jin ran dian jiang di .
论文参考文献
论文详细介绍
论文作者分别是来自东北大学学报(自然科学版)的程春龙,乐启炽,发表于刊物东北大学学报(自然科学版)2019年09期论文,是一篇关于燃点论文,系镁合金论文,热解论文,初始熔化温度论文,扫描电子显微镜论文,东北大学学报(自然科学版)2019年09期论文的文章。本文可供学术参考使用,各位学者可以免费参考阅读下载,文章观点不代表本站观点,资料来自东北大学学报(自然科学版)2019年09期论文网站,若本站收录的文献无意侵犯了您的著作版权,请联系我们删除。
标签:燃点论文; 系镁合金论文; 热解论文; 初始熔化温度论文; 扫描电子显微镜论文; 东北大学学报(自然科学版)2019年09期论文;