本文主要研究内容
作者（2019）在《Preparation of SGO-modified nanofiltration membrane and its application in SO42- and Cl- separation in salt treatment》一文中研究指出：The lack of fresh water in the world makes the search for an effective method to decontaminate water an urgent priority.An important step is to remove different multivalent ions in salt treatment.Nanofiltration（NF）has been used for treating water containing different kinds of salts.In this work,sulfonate group-modified graphene oxide（SGO）was prepared,and added during the interfacial polymerization（IP）reaction to prepare SGO-modifiedNF membranes（PA-SGO）.The chemical composition,structure and surface properties of PA and PA-SGO membranes were characterized by FT-IR,XPS,SEM,AFM,contact angle and zeta potential measurements.Their water flux,salt rejection and antifouling abilities were investigated systematically.The testing results showed that the water flux of PA-SGO（0.03%SGO）was 45.85 LMH under a pressure of 0.2 MPa,and the salt rejection varied in the order of Na2SO4（98.99%）>MgSO4（91.25%）>MgCl2（42.27%）>NaCl（21.96%）.An anti-fouling experiment indicated that the PA-SGO membrane had good anti-fouling properties because of its decreased roughness and increased hydrophilicity and electronegativity.The PA-SGO membrane has good potential for use in removing salt ions from water.
Abstract
The lack of fresh water in the world makes the search for an effective method to decontaminate water an urgent priority.An important step is to remove different multivalent ions in salt treatment.Nanofiltration（NF）has been used for treating water containing different kinds of salts.In this work,sulfonate group-modified graphene oxide（SGO）was prepared,and added during the interfacial polymerization（IP）reaction to prepare SGO-modifiedNF membranes（PA-SGO）.The chemical composition,structure and surface properties of PA and PA-SGO membranes were characterized by FT-IR,XPS,SEM,AFM,contact angle and zeta potential measurements.Their water flux,salt rejection and antifouling abilities were investigated systematically.The testing results showed that the water flux of PA-SGO（0.03%SGO）was 45.85 LMH under a pressure of 0.2 MPa,and the salt rejection varied in the order of Na2SO4（98.99%）>MgSO4（91.25%）>MgCl2（42.27%）>NaCl（21.96%）.An anti-fouling experiment indicated that the PA-SGO membrane had good anti-fouling properties because of its decreased roughness and increased hydrophilicity and electronegativity.The PA-SGO membrane has good potential for use in removing salt ions from water.
论文参考文献
论文详细介绍
论文作者分别是来自Journal of Environmental Sciences的，发表于刊物Journal of Environmental Sciences2019年04期论文，是一篇关于,Journal of Environmental Sciences2019年04期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Journal of Environmental Sciences2019年04期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。