作者（2019）在《Cleaning of high antimony smelting slag from an oxygen-enriched bottom-blown by direct reduction》一文中研究指出：Cleaning of high antimony smelting slag from an oxygen-enriched bottom-blown was tested by direct reduction in a laboratory-scale electric furnace.The effects of added CaO,mass ratio of coal（experimental）to coal（theoretical）（ω）and the slag type on the reduction procedure were considered.The contents of Sb and Au were investigated.Iron contamination of the metal phase was analyzed as this may impede the economical viability of this process.The initial slag,coal and CaO were mixed and homogenized before charging into the furnace,and the residual slag averagely contains 1.26 g.ton-1 Au and1.17 wt% Sb.However,the iron contamination of antimony alloy becomes unacceptably high in this case as the metal phases contain up to 10 wt% Fe.In the slag system with mass ratio of SiO2:FeO:CaO= 45:27:18,the residual slag obtained after reduction under these conditions averagely contains<1 g·ton-1 Au and<1 wt% Sb,and the metal phase contains<7 wt% Fe.The recoveries of Au in the metal phase are>98 % in all experiments which is proved to be an economic and cleaning process.
Abstract
Cleaning of high antimony smelting slag from an oxygen-enriched bottom-blown was tested by direct reduction in a laboratory-scale electric furnace.The effects of added CaO,mass ratio of coal（experimental）to coal（theoretical）（ω）and the slag type on the reduction procedure were considered.The contents of Sb and Au were investigated.Iron contamination of the metal phase was analyzed as this may impede the economical viability of this process.The initial slag,coal and CaO were mixed and homogenized before charging into the furnace,and the residual slag averagely contains 1.26 g.ton-1 Au and1.17 wt% Sb.However,the iron contamination of antimony alloy becomes unacceptably high in this case as the metal phases contain up to 10 wt% Fe.In the slag system with mass ratio of SiO2:FeO:CaO= 45:27:18,the residual slag obtained after reduction under these conditions averagely contains<1 g·ton-1 Au and<1 wt% Sb,and the metal phase contains<7 wt% Fe.The recoveries of Au in the metal phase are>98 % in all experiments which is proved to be an economic and cleaning process.
论文参考文献
论文详细介绍
论文作者分别是来自Rare Metals的，发表于刊物Rare Metals2019年08期论文，是一篇关于,Rare Metals2019年08期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Rare Metals2019年08期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。