作者（2019）在《Comparison of performance of Ni-Mo/γ-alumina catalyst in HDS and HDN reactions of main distillate fractions》一文中研究指出：A bimetallic nickel-molybdenum catalyst supported on γ-alumina was synthesized by the two-step incipient wetness impregnation technique.The activity of the prepared Ni-Mo/γ-alumina catalyst was evaluated in a down flow fixed-bed microreactor.In this way,hydrodesulfurization(HDS)and hydrodenitrogenation(HDN)reactions of the main distillate fractions of crude oil were assessed.XRD,SEM,TPR,ICP-OES,BET-BJH and nitrogen adsorption/desorption methods were used for characterizing the synthesized Ni-Mo/γ-alumina catalyst.The active metals with Ni/Mo mass ratio of 0.23 and total metal of 13.7 wt% were loaded on the support,similar to the commercial industrial catalyst.The performance tests were conducted at 3.0 MPa(for light naphtha and heavy naphtha)and at 4.5 MPa(for kerosene and gas oil).The results revealed that the total sulfur conversion of the light naphtha,heavy naphtha,kerosene and gas oil fractions was 98.3%,95%,91.7% and 90.1%(after 24 h),respectively.
Abstract
A bimetallic nickel-molybdenum catalyst supported on γ-alumina was synthesized by the two-step incipient wetness impregnation technique.The activity of the prepared Ni-Mo/γ-alumina catalyst was evaluated in a down flow fixed-bed microreactor.In this way,hydrodesulfurization(HDS)and hydrodenitrogenation(HDN)reactions of the main distillate fractions of crude oil were assessed.XRD,SEM,TPR,ICP-OES,BET-BJH and nitrogen adsorption/desorption methods were used for characterizing the synthesized Ni-Mo/γ-alumina catalyst.The active metals with Ni/Mo mass ratio of 0.23 and total metal of 13.7 wt% were loaded on the support,similar to the commercial industrial catalyst.The performance tests were conducted at 3.0 MPa(for light naphtha and heavy naphtha)and at 4.5 MPa(for kerosene and gas oil).The results revealed that the total sulfur conversion of the light naphtha,heavy naphtha,kerosene and gas oil fractions was 98.3%,95%,91.7% and 90.1%(after 24 h),respectively.
论文参考文献
论文详细介绍
论文作者分别是来自Petroleum Science的，发表于刊物Petroleum Science2019年03期论文，是一篇关于,Petroleum Science2019年03期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Petroleum Science2019年03期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。