本文主要研究内容
作者（2019）在《Study on Glass Fiber Dispersion Technology in SiO2 Aerogel-glass Fiber Composite Insulation Materials》一文中研究指出：In order to improve the mechanical properties of SiO2 aerogel-glass fiber composites, effects of different solvents（cyclohexane, n-hexane, ethanol, acetone） and different dispersing modes（planetary ball milling, ultrasonic dispersion and mechanical stirring） and dispersing duration（10-40 min） on the dispersion of chopped alkali-free glass fiber bundles were studied to determine the best dispersion process. On this basis, the materials were batched according to the mass fraction of SiO2 aerogel powder to chopped alkali free glass fiber bundles of 90:10, and a certain amount of zinc oxide light-screening agent and phenolic resin binder were added. SiO2 aerogel glass fiber composite specimens were prepared by direct adding chopped alkali free glass fiber bundles and pre-dispersed chopped alkali free glass fiber bundles, respectively. The cold crushing strength and the thermal conductivity at different surface temperatures（300, 400, 500 and 600 ℃, respectively）of the specimens were measured. The results show that:（1） the optimum dispersion process of chopped alkali-free glass fiber bundles is using ethanol as solvent and mechanical stirring for 30 min;（2） pre-dispersion of chopped alkali-free glass fiber bundles has little effect on the thermal conductivity of SiO2 aerogel-glass fiber composites but can improve the cold crushing strength.
Abstract
In order to improve the mechanical properties of SiO2 aerogel-glass fiber composites, effects of different solvents（cyclohexane, n-hexane, ethanol, acetone） and different dispersing modes（planetary ball milling, ultrasonic dispersion and mechanical stirring） and dispersing duration（10-40 min） on the dispersion of chopped alkali-free glass fiber bundles were studied to determine the best dispersion process. On this basis, the materials were batched according to the mass fraction of SiO2 aerogel powder to chopped alkali free glass fiber bundles of 90:10, and a certain amount of zinc oxide light-screening agent and phenolic resin binder were added. SiO2 aerogel glass fiber composite specimens were prepared by direct adding chopped alkali free glass fiber bundles and pre-dispersed chopped alkali free glass fiber bundles, respectively. The cold crushing strength and the thermal conductivity at different surface temperatures（300, 400, 500 and 600 ℃, respectively）of the specimens were measured. The results show that:（1） the optimum dispersion process of chopped alkali-free glass fiber bundles is using ethanol as solvent and mechanical stirring for 30 min;（2） pre-dispersion of chopped alkali-free glass fiber bundles has little effect on the thermal conductivity of SiO2 aerogel-glass fiber composites but can improve the cold crushing strength.
论文参考文献
论文详细介绍
论文作者分别是来自China’s Refractories的，发表于刊物China’s Refractories2019年01期论文，是一篇关于,China’s Refractories2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自China’s Refractories2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。