作者（2019）在《Humidity-responsive Bilayer Actuators Comprised of Porous and Nonporous Poly(acrylic acid)/Poly(allylamine hydrochloride) Films》一文中研究指出：Bilayer humidity-responsive actuators are generally composed of actuating and supporting layers of different materials with largely different wettability.Such kinds of bilayer actuators suffer from low adhesive force between the two layers during usage.This study demonstrates the preparation of humidity-responsive bilayer actuators that have the same materials in the actuating and supporting layers to avoid the adhesive issue.The bilayer actuators consist of a porous poly(acrylic acid)(PAA)/poly(allylamine hydrochloride)(PAH)layer and a nonporous PAA/PAH layer that are fabricated by exponentially layer-by-layer assembly method.At a high/low relative humidity(RH),the nonporous PAA/PAH layer can efficiently expand/shrink by absorbing/desorbing water while the volume expansion/shrinkage of the porous PAA/PAH layer in an environment with changed humidity is significantly suppressed by the micrometer-sized pores.The largely different expansion/shrinkage of the nonporous and porous PAA/PAH layers when subjected to humidity changes enables rapid and reversible rolling/unrolling motions of the bilayer actuator.The bilayer actuator shows a faster rolling speed and a larger bending curvature when subjected to a larger humidity increase.
Abstract
Bilayer humidity-responsive actuators are generally composed of actuating and supporting layers of different materials with largely different wettability.Such kinds of bilayer actuators suffer from low adhesive force between the two layers during usage.This study demonstrates the preparation of humidity-responsive bilayer actuators that have the same materials in the actuating and supporting layers to avoid the adhesive issue.The bilayer actuators consist of a porous poly(acrylic acid)(PAA)/poly(allylamine hydrochloride)(PAH)layer and a nonporous PAA/PAH layer that are fabricated by exponentially layer-by-layer assembly method.At a high/low relative humidity(RH),the nonporous PAA/PAH layer can efficiently expand/shrink by absorbing/desorbing water while the volume expansion/shrinkage of the porous PAA/PAH layer in an environment with changed humidity is significantly suppressed by the micrometer-sized pores.The largely different expansion/shrinkage of the nonporous and porous PAA/PAH layers when subjected to humidity changes enables rapid and reversible rolling/unrolling motions of the bilayer actuator.The bilayer actuator shows a faster rolling speed and a larger bending curvature when subjected to a larger humidity increase.
论文参考文献
论文详细介绍
论文作者分别是来自Chinese Journal of Polymer Science的，发表于刊物Chinese Journal of Polymer Science2019年01期论文，是一篇关于,Chinese Journal of Polymer Science2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Chinese Journal of Polymer Science2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。