本文主要研究内容
作者罗西希,姚正军（2019）在《Laser Cladding Fe-Al-Cr Coating with Enhanced Mechanical Properties》一文中研究指出：Dense Fe-Al-Cr coatings with approximately 50 μm in thickness are successfully prepared on the 1045 carbon steel substrates via a laser cladding process. Proper Cr content(5 at% Cr) will lead to decrease in the melting point, and improves the viscosity of the liquid and the nucleation rate of the molten pool, leading to refining grains of the solidification structure. As a result, the Fe-29 Al-5 Cr laser cladding layer exhibits the best hardness, plasticity properties, and wear resistance at 400 °C. Excessive Cr for the Fe-29 Al-7.5 Cr coating leads to the formation of Cr2 Al in the grain boundaries and thermal vacancies during the solidification process, resulting in inferior mechanical properties and poor tribological behavior.
Abstract
Dense Fe-Al-Cr coatings with approximately 50 μm in thickness are successfully prepared on the 1045 carbon steel substrates via a laser cladding process. Proper Cr content(5 at% Cr) will lead to decrease in the melting point, and improves the viscosity of the liquid and the nucleation rate of the molten pool, leading to refining grains of the solidification structure. As a result, the Fe-29 Al-5 Cr laser cladding layer exhibits the best hardness, plasticity properties, and wear resistance at 400 °C. Excessive Cr for the Fe-29 Al-7.5 Cr coating leads to the formation of Cr2 Al in the grain boundaries and thermal vacancies during the solidification process, resulting in inferior mechanical properties and poor tribological behavior.
论文参考文献
论文详细介绍
论文作者分别是来自Journal of Wuhan University of Technology(Materials Science)的罗西希,姚正军，发表于刊物Journal of Wuhan University of Technology(Materials Science)2019年05期论文，是一篇关于,Journal of Wuhan University of Technology(Materials Science)2019年05期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自Journal of Wuhan University of Technology(Materials Science)2019年05期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：Journal of Wuhan University of Technology(Materials Science)2019年05期论文;