作者（2019）在《Mechanical Properties of Carbon Epoxy Prepreg Insert Phenolic Resin Injection Moldings》一文中研究指出：This study focuses on the insert-injection molding process. The thermoset composite inserts in this study were carbon fiber/epoxy(CF/Epoxy) prepreg sheets. The injected molded part was glass fiber contained phenolic resin(GF/PF). The CF/Epoxy was placed in the mold cavity prior to injecting GF/PF onto the inserted injection molded CF/Epoxy specimens. The role of adhesion between the inserted part and injected resin on the mechanical properties was evaluated by 3 point bending and impact tests. In addition, the effect of prepreg orientation on the mechanical properties of the prepreg inserted-injection molding system was investigated. It was found that the prepreg with unidirectional orientation significantly improved flexural and impact strength of the inserted injection molding composites, providing better support and resistance to bending and impact loading. The main failure modes of the specimens were structural and adhesive failure.
Abstract
This study focuses on the insert-injection molding process. The thermoset composite inserts in this study were carbon fiber/epoxy(CF/Epoxy) prepreg sheets. The injected molded part was glass fiber contained phenolic resin(GF/PF). The CF/Epoxy was placed in the mold cavity prior to injecting GF/PF onto the inserted injection molded CF/Epoxy specimens. The role of adhesion between the inserted part and injected resin on the mechanical properties was evaluated by 3 point bending and impact tests. In addition, the effect of prepreg orientation on the mechanical properties of the prepreg inserted-injection molding system was investigated. It was found that the prepreg with unidirectional orientation significantly improved flexural and impact strength of the inserted injection molding composites, providing better support and resistance to bending and impact loading. The main failure modes of the specimens were structural and adhesive failure.
论文参考文献
论文详细介绍
论文作者分别是来自纤维复合材料的，发表于刊物纤维复合材料2019年02期论文，是一篇关于,纤维复合材料2019年02期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自纤维复合材料2019年02期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：纤维复合材料2019年02期论文;