本文主要研究内容

作者刘娇,丁亮,吴亮,徐铜文(2019)在《电场辅助制备分层多孔扩散渗析膜》一文中研究指出:传统的扩散渗析膜厚度较大,传质阻力较大,使得氢离子较难透过,酸回收率不高.本文通过采用外加电场辅助致密膜成孔的方法,探讨了电场强度和作用时间对聚(QVBC-DVB)/PVDF离子交换膜形貌的影响,制备出"三明治"型分层多孔扩散渗析膜,将致密层厚度从80.0μm降低至46.8μm.扩散渗析测试表明,经100 mA/cm2的电场作用72 h后,氢离子渗析系数和分离因子分别达到12.12×10-3m/h和198,与致密基膜相比分别提高了121.7%和57.1%,为改善扩散渗析膜性能提供了新思路.

Abstract

chuan tong de kuo san shen xi mo hou du jiao da ,chuan zhi zu li jiao da ,shi de qing li zi jiao nan tou guo ,suan hui shou lv bu gao .ben wen tong guo cai yong wai jia dian chang fu zhu zhi mi mo cheng kong de fang fa ,tan tao le dian chang jiang du he zuo yong shi jian dui ju (QVBC-DVB)/PVDFli zi jiao huan mo xing mao de ying xiang ,zhi bei chu "san ming zhi "xing fen ceng duo kong kuo san shen xi mo ,jiang zhi mi ceng hou du cong 80.0μmjiang di zhi 46.8μm.kuo san shen xi ce shi biao ming ,jing 100 mA/cm2de dian chang zuo yong 72 hhou ,qing li zi shen xi ji shu he fen li yin zi fen bie da dao 12.12×10-3m/hhe 198,yu zhi mi ji mo xiang bi fen bie di gao le 121.7%he 57.1%,wei gai shan kuo san shen xi mo xing neng di gong le xin sai lu .

论文参考文献

  • [1].离子交换膜的应用技术[J]. 耿道静,李红海.  当代化工.2017(12)
  • [2].离子交换膜及其在水处理中的应用[J]. 高教成.  科技资讯.2014(31)
  • [3].扩散渗析总传质系数计算式的推导与探讨[J]. 刘亚飞,李传润,徐铜文.  膜科学与技术.2013(02)
  • [4].扩散渗析用阴离子交换膜的研制[J]. 钱锦棠,王淑英,张世枚,罗腊生.  塑料工业.1984(01)
  • [5].扩散渗析-电沉积联合工艺资源回收酸性含铜树脂脱附液[J]. 王刚,张炜铭,杨柽瀚,王劲松,虢清伟,邴永鑫,孙平,吕路,潘丙才.  膜科学与技术.2017(05)
  • [6].聚氯乙烯半均相离子交换膜[J].   塑料工业.1978(04)
  • [7].离子交换膜分离技术在冶金中的应用[J]. 张启修,张传福.  膜科学与技术.2001(02)
  • [8].离子交换膜的发展态势与应用展望[J]. 葛倩倩,葛亮,汪耀明,徐铜文.  化工进展.2016(06)
  • [9].离子交换膜的制造和应用[J]. 吴勇.  浙江化工.1984(04)
  • [10].离子交换膜技术的应用[J]. 王津.  福建化工.2002(02)
  • 论文详细介绍

    论文作者分别是来自膜科学与技术的刘娇,丁亮,吴亮,徐铜文,发表于刊物膜科学与技术2019年03期论文,是一篇关于离子交换膜论文,扩散渗析论文,电场论文,传质阻力论文,膜科学与技术2019年03期论文的文章。本文可供学术参考使用,各位学者可以免费参考阅读下载,文章观点不代表本站观点,资料来自膜科学与技术2019年03期论文网站,若本站收录的文献无意侵犯了您的著作版权,请联系我们删除。

    标签:;  ;  ;  ;  ;  

    刘娇:电场辅助制备分层多孔扩散渗析膜论文
    下载Doc文档

    猜你喜欢