作者徐孝轩,朱原原,付安庆,肖雯雯,杨志文,闫智伦（2019）在《酸性油气田C110套管断裂失效分析》一文中研究指出：为查明酸性油气田某油井C110套管断裂失效原因,通过C110断裂失效套管断口宏观形貌、金相组织、化学成分、力学性能和腐蚀产物成分等综合分析,对酸性油气田某油井C110套管断裂原因进行了探讨。结果表明:套管不居中导致套管产生应力集中,并在套管与卡瓦咬合的第1个齿形成严重机械损伤;同时,地层运动、套压波动等因素导致套管在应力集中部位出现交变载荷。最终,在套管内壁处于高H2S、低p H值环境下,在内表面交变应力集中区域发生腐蚀疲劳开裂。
wei cha ming suan xing you qi tian mou you jing C110tao guan duan lie shi xiao yuan yin ,tong guo C110duan lie shi xiao tao guan duan kou hong guan xing mao 、jin xiang zu zhi 、hua xue cheng fen 、li xue xing neng he fu shi chan wu cheng fen deng zeng ge fen xi ,dui suan xing you qi tian mou you jing C110tao guan duan lie yuan yin jin hang le tan tao 。jie guo biao ming :tao guan bu ju zhong dao zhi tao guan chan sheng ying li ji zhong ,bing zai tao guan yu ka wa yao ge de di 1ge chi xing cheng yan chong ji xie sun shang ;tong shi ,de ceng yun dong 、tao ya bo dong deng yin su dao zhi tao guan zai ying li ji zhong bu wei chu xian jiao bian zai he 。zui zhong ,zai tao guan nei bi chu yu gao H2S、di p Hzhi huan jing xia ,zai nei biao mian jiao bian ying li ji zhong ou yu fa sheng fu shi pi lao kai lie 。
论文作者分别是来自材料保护的徐孝轩,朱原原,付安庆,肖雯雯,杨志文,闫智伦，发表于刊物材料保护2019年03期论文，是一篇关于酸性油气田论文,套管论文,腐蚀疲劳开裂论文,失效分析论文,材料保护2019年03期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自材料保护2019年03期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
本文来源: https://www.lw00.cn/article/57baa78475c3d63ba44fc613.html