邵斌：0.2%氢对Ti-22Al-25Nb合金O相转变和B2相再结晶的影响论文

本文主要研究内容

作者邵斌,单德彬,郭斌,宗影影（2019）在《0.2%氢对Ti-22Al-25Nb合金O相转变和B2相再结晶的影响》一文中研究指出：通过对Ti-22Al-25Nb合金置氢,研究氢对Ti-22Al-25Nb合金O转变及B2再结晶过程的影响。结果表明,在添加质量分数0.2%的氢后Ti-22Al-25Nb合金的热处理过程中,相变过程加快,相变点降低。并且氢促进B2相再结晶过程,960℃时的晶粒尺寸从135μm细化到60μm。在升温过程中氢促进强化相O相分解为B2相,并促进α2相从颗粒状转变为条状。在750℃保温时氢促进O相在晶界处优先析出并迅速长大,氢加快了B2→O相的转变过程。

Abstract

tong guo dui Ti-22Al-25Nbge jin zhi qing ,yan jiu qing dui Ti-22Al-25Nbge jin Ozhuai bian ji B2zai jie jing guo cheng de ying xiang 。jie guo biao ming ,zai tian jia zhi liang fen shu 0.2%de qing hou Ti-22Al-25Nbge jin de re chu li guo cheng zhong ,xiang bian guo cheng jia kuai ,xiang bian dian jiang di 。bing ju qing cu jin B2xiang zai jie jing guo cheng ,960℃shi de jing li che cun cong 135μmxi hua dao 60μm。zai sheng wen guo cheng zhong qing cu jin jiang hua xiang Oxiang fen jie wei B2xiang ,bing cu jin α2xiang cong ke li zhuang zhuai bian wei tiao zhuang 。zai 750℃bao wen shi qing cu jin Oxiang zai jing jie chu you xian xi chu bing xun su chang da ,qing jia kuai le B2→Oxiang de zhuai bian guo cheng 。

论文参考文献

[1].α2+B2相区等温锻造及热处理对Ti-22Al-25Nb合金组织和性能的影响[J]. 梁晓波,马雄,张建伟,程云君,曾卫东,王伟. 钛工业进展.2018(01)

[2].热处理对B2相区等温锻造Ti-22Al-25Nb合金组织和性能的影响[J]. 董志国,李冬,曾卫东,王伟,梁晓波. 钛工业进展.2018(03)

[3].高钼无钴马氏体时效合金的再结晶[J]. 任怀亮,高伟,杨让. 物理测试.1987(05)

[4].再结晶对沉淀粒子尺寸及其分布的影响[J]. 刘伟. 中南矿冶学院学报.1987(03)

[5].微量锆对导电用工业纯铝再结晶的影响研究[J]. 周善佑,张萍. 镇江船舶学院学报.1988(Z1)

[6].再结晶加热速率对LC9超硬铝晶粒细化的影响[J]. 唐国宏,宋作舟,吴云书. 北京航空学院学报.1988(03)

[7].稀土元素对银的再结晶及晶粒组织的影响[J]. 黎鼎鑫,秦国义. 贵金属.1988(04)

[8].铁及低碳钢的超快速退火[J]. 施华,M.Atkinson. 东北工学院学报.1989(03)

[9].18Ni合金在弹性应力作用下再结晶诱发塑性现象[J]. 尹钟大,周永康. 金属学报.1989(05)

[10].关于深冲薄板退火过程中的再结晶机制问题[J]. 胡玉和. 鞍钢技术.1989(06)

论文详细介绍

论文作者分别是来自稀有金属材料与工程的邵斌,单德彬,郭斌,宗影影，发表于刊物稀有金属材料与工程2019年04期论文，是一篇关于合金论文,氢致相变论文,晶粒细化论文,稀有金属材料与工程2019年04期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自稀有金属材料与工程2019年04期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。

本文来源: https://www.lw00.cn/article/7c92d1a4eaafecbd91350664.html