作者王成猛,姚兆凤,牛建宇,梁梦斐,王海燕（2019）在《热轧工艺对400 MPa汽车钢板显微组织和硬度的影响》一文中研究指出：针对热轧400 MPa汽车钢板制定了合理的热轧工艺参数.通过金相和扫描电镜观察,考察了轧制前后的显微组织变化情况;采用Image Tool分析软件,统计分析了轧制前后的晶粒尺寸分布.结合硬度测试结果,分析了400 MPa汽车钢板热轧后的硬度与强度.结果表明,热轧后实验钢组织主要为等轴状铁素体+珠光体+贝氏体.添加稀土实验钢与不加稀土实验钢相比,组织更加细小均匀.与轧制前钢板硬度相比,实验钢硬度有所提高.
zhen dui re ga 400 MPaqi che gang ban zhi ding le ge li de re ga gong yi can shu .tong guo jin xiang he sao miao dian jing guan cha ,kao cha le ga zhi qian hou de xian wei zu zhi bian hua qing kuang ;cai yong Image Toolfen xi ruan jian ,tong ji fen xi le ga zhi qian hou de jing li che cun fen bu .jie ge ying du ce shi jie guo ,fen xi le 400 MPaqi che gang ban re ga hou de ying du yu jiang du .jie guo biao ming ,re ga hou shi yan gang zu zhi zhu yao wei deng zhou zhuang tie su ti +zhu guang ti +bei shi ti .tian jia xi tu shi yan gang yu bu jia xi tu shi yan gang xiang bi ,zu zhi geng jia xi xiao jun yun .yu ga zhi qian gang ban ying du xiang bi ,shi yan gang ying du you suo di gao .
论文作者分别是来自内蒙古科技大学学报的王成猛,姚兆凤,牛建宇,梁梦斐,王海燕，发表于刊物内蒙古科技大学学报2019年01期论文，是一篇关于汽车钢论文,热轧工艺论文,显微组织论文,硬度论文,内蒙古科技大学学报2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自内蒙古科技大学学报2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
本文来源: https://www.lw00.cn/article/d79a9cf3008e5909d69cd52c.html